Table of Contents
ePA is developed based on nylon 6/66 copolymer; Self-lubricating wear resistance makes it suitable for printing gears; High toughness and impact resistance, with an elongation at break of up to 175%, which can print strong and durable parts with high fracture resistance; Low shrinkage, not easy to warp and crack when printing.
Sellingpoint #
High toughness
High impact resistance
Self-lubricating wear-resisting
Excellent printability
| Filament Properties Table | |
|---|---|
| 3D PRINTING FILAMENT | ePA |
| Density(g/cm3) | 1.12 |
| Heat Distortion Temp(℃,0.45MPa) | 50 |
| Melt Flow Index(g/10min) | 12.3(230℃/2.16kg) |
| Tensile Strength(MPa) | 52.45 |
| Elongation at Break(%) | 175.32 |
| Flexural Strength(MPa) | 58 |
| Flexural Modulus(MPa) | 1370 |
| IZOD Impact Strength(kJ/㎡) | 18.4 |
| Durability | 10/10 |
| Printability | 8/10 |
| Recommended printing parameters | |
| Extruder Temperature(℃) | 260 – 290℃ Recommended temperature：280℃ |
| Bed temperature(℃) | 70 – 90°C |
| Fan Speed | 0% |
| Printing Speed | 40 – 100mm/s |
| Heated Bed | Required |
| Recommended Build Surfaces | Solid glue, PEI |
| Feature | |
| Flexible | √ |
| Elastic | —— |
| Impact Resistant | √ |
| Soft | —— |
| Composite | —— |
| UV Resistant | —— |
| Water Resistant | —— |
| Dissolvable | —— |
| Heat Resistant | √ |
| Chemically Resistant | —— |
| Fatigue Resistant | √ |
| Need drying | √ |
| Heated Bed Required | √ |
| Print recommend | Drying at 70℃/>12h |